Comparison of thermal/mechanical properties and shape memory effect of
polyurethane block-copolymers with planar or bent shape of hard segment
出處:Received 31 December 2002; received in revised form
13March 2003; accepted 27 March 2003
作者:Jae Heung Yang, Byoung Chul Chun, Yong-Chan Chung,
Jae Hwan Cho
簡報日期:100.11.14
摘要
A series of shape memory polyurethane copolymers synthesized from 1,4-phenyldiisocyanate (PDI) and poly(tetramethyleneglycol) (PTMG) plus 1,4-butanediol as chain extender were compared with similar ones from 4,40-methylene-bis-phenyldiisocyanate (MDI) and PTMG in various shape memory tests at temperature ranges of ^20 8C around glass transition temperature ðTgÞ: Similarity and some differences between two series were found in other characterization methods such as IR spectra, phase transition,and mechanical properties. Especially, Tg increased with the content of hard segment (PDI or MDI) and both copolymers generally showed similar Tg at the same content
of hard segment. In addition, vibration and shock absorption ability was investigated by measuring both loss tan d and storage modulus with dynamic mechanical analyzer.
of hard segment. In addition, vibration and shock absorption ability was investigated by measuring both loss tan d and storage modulus with dynamic mechanical analyzer.